Common Lamination Problems

The most common cause of bubbling on the laminate is insufficient tension when laminating.

Common lamination problems.

The same principles apply to cold laminates. Why isn t my film sticking properly. Silvering is caused when the adhesive not wetting out properly this problem is solved by either increasing the temperature setting or slowing down the speed setting. This situation can be easily remedied.

Make sure the ink is dry leave time for the print to cure before laminating. Infeed waves are mars in the finished product that result from the original image being somehow distorted. Phone before sending in the samples. Lamination is all about getting two materials to bond together.

What some people have described to us as wrinkling was what we would call waviness or some other problem such as a repeating impression on the surface of the finished lamination. You can try laminating the document again this time applying a little more tension on the machine ideally based on the pouch s specifications. Industry expert david goetter shows a brand new over laminate material from advanced greig laminators. This will promote a better adhesive flow.

The biggest pitfalls for laminators has been the same one that has dogged converters since the dawn of well lamination. When you try to finish straight off the back of digital print you re more likely to have issues with film sticking. Sometimes the best way to identify the nature of a defect is to mail or overnight samples to us. My laminating pouch appears cloudy even after going through the machine.

Some of the most common problems with laminated prints due to the wrong amount of tension or pressure are as follows. If you have cool spots on the product it means there s an area on the roll that s not hot enough to melt the adhesive. Having the right set up right from the start. This material is one of my personal favorites because.

Below is a list of some of the most frequently encountered laminating problems and tips on how to remedy them. Sometimes you may need to do both. Infeed waves are mars in the finished product that result from the original image being somehow distorted before it went in. When you start laminating from cold you risk having different temperatures on parts of the roll which affects the quality of the finishing.